H13 Material Prices that Meet Your Budget and Needs

We, as an h13 material price supplier, started in August 2007 and began operations. It is situated next to the Xisaishan Industrial Park, which is known as “the cradle of steel” and is situated in Huangshi City, Hubei Province. However, we as an h13 material price manufacturer, have a workshop area of 40,000 square meters and a 65-acre footprint. Tool steel output ranges from 2000 tons per month to 25000 tons annually.

We, as an h13 material price supplier also boast an experienced export team and technical expertise. Therefore, it uses to offer customers expert technical guidance and support. We provide premium H13 material at competitive prices to satisfy your unique needs. Known for its exceptional heat resistance, toughness, and wear resistance, H13 is a useful tool for steel.

H13 Material Price Manufacturer

We, as an h13 material price manufacturer, provide quality that is frequently used in processes like die casting, forging, extrusion, and hot stamping. Mainly because of how well it performs at high temperatures. H13 material is a well-liked selection for numerous tooling and machining applications, regardless of whether you work in the automotive, aerospace, or manufacturing industries. However, we recognize the value of being cost-effective without sacrificing quality.

We, as an h13 material price supplier, provide affordable H13 material costs that take into account your financial limitations and guarantee you’ll get supplies that adhere to industry requirements. To ensure that it reaches the highest requirements, our H13 material is purchased from reliable mills and put through stringent quality inspections. We, as h13 material price manufacturer, recognize that every project is different. Therefore, to meet your precise requirements, we provide customizable choices as aisi h13 supplier.

Best Aisi H13 Supplier In The Market

We are a significant aisi H13 supplier private company that specializes in the manufacture (TTSCO), processing, and selling of several types of special steel. However, we have been certified as meeting the requirements of the ISO 9001 Quality Management System. Thus, to provide a sufficient supply of Plastic Mold Steel, we as aisi h13 manufacturer, have invested in Steel Mills (TTSCO) in the north and middle of China.

We, as aisi h13 supplier, have unrivaled experience in creating and selling AISI H13 tool steel thanks to years of industry experience. Therefore, each product is meticulously created by our team of experts, ensuring dependability and longevity. However, at the core of all we do is quality. Modern technologies and strict quality control procedures are used to produce our AISI H13 steel.

How is the H13 material heating process?

Preheating H13 tool steels to 816°C (1500°F).

Can H13 be machined easily?

H13 is very challenging to machine because of its high hardness and toughness.

How is the H13 material hardness?

Hardening: 780–820°C for preheating. Completely soak, then quickly raise temperature to the final hardness range of 1000–1030°

How tough is H13 without heat treatment?

H13 is useful in the HRC 38 to 48 hardness range for hot work applications.

How is the H13 material hardened?

Hardening: 780–820°C for preheating. Completely soak, then quickly raise temperature to the final hardness range of 1000–1030°C.

How hard is H13 at its hardest?

 The standard delivery condition for H13 is annealing. Max. 235 HB for H13 Harness after annealing


Product Overviews


H13 is a chromium, molybdenum, vanadium hot work tool steel which is characterized by high hardenability and excellent toughness. The molybdenum and vanadium act as strengthening agents. The chromium content assists H-13 to resist softening when used at high temperatures. H-13 offers an excellent combination of shock and abrasion resistance, and possesses good red hardness. It is capable of withstanding rapid cooling and resists premature heat checking. H-13 has good machinability, good weldability, good ductility, and can be formed by conventional means.

Specification  :

Size round Dia 15mm~500mm
flat Thickness  10mm-400mm
Width   60mm-810mm
Technique Cold Drawn/Cold Pilfered/Cold Rolled/Hot Rolled/forge-
Process EAF+LF+VD+ESR+Forged/Hot rolled + Heat Treatment (Annealed, Normalized, Q+T)
Heat treatment Normalized ; Annealed ; Quenched ; Tempered
Surface Condition Black surface ; Grinded ; Machined/Turned
Inspection 100% Ultrasonic according to the test standards:SEP1921-84,CLASS C/c or D/d
Payment Terms T/T; L/C
Trade Terms FOB,CIF,CFR
Packing Standard seaworthy packing or as customer required

 Equivalent  Grade :

4Cr5MoSiV1 H13 1.2344 SKD61 X40CrMoV5-1

Chemical Composition :

C Si Mn Cr Mo V P S
0.32-0.45 0.8-1.2 0.2-0.5 4.75~5.50 1.1-1.75 0.8-1.2 ≤0.030 ≤0.030

 Heat treatment :

Heat Treatment
Forging Preheat slowly to 750°C then increase the temperature more rapidly to 1050-1100 °C. Do not forge below 850°C. It is essential to cool the H13 slowly after forging, either in a furnace or in vermiculite
Annealing Soak thoroughly at 840-860°C before furnace cooling at a maximum rate of 20°C per hour down to 600°C followed by cooling in air.
Stress relieving When desirable to relieve the strains of machining, heat slowly to 1050°-1250°F, allow to equalize,and then cool in still air (Strain Relieving)
Preheat prior to hardening Warm slightly before charging into the preheat furnace, which should be operating at 1400°-1500°F.
Hardening H13 is a steel having very high hardenability and should be hardened by cooling in still air. The use of a salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening in spent pitch coke is suggested. The temperature employed is usually 1800°-1850°F, depending on size section.
Quenching Quench in still air or dry air blast. If complicated forms are to be hardened, an interrupted oil quench can be used. Quench part in oil and remove from bath when it just loses its color (1000°-1100°F). Finish cooling to below 150°-125°F in air, then temper immediately.
Tempering Tempering practice may vary with size and application, but is usually performed in the range of maximum secondary hardness or higher. Double tempering is recommended. The results below is H13 that was air quenched from 1800°F and tempered for 4 hours at various temperatures.The results may be used as a guide, keeping in mind that parts of heavy section or mass may be several points lower in hardness.
Applications Typical applications for are forging dies, forging die inserts, hot gripper dies, hot nut tools, hot header dies, brass forging and pressing dies, aluminum base dies, aluminum casting and extrusion dies, zinc die casting dies, extrusion mandrels, plastic molds, cores, die holder blocks, hot press dies, hot work punches, etc.

Applications include:

  • Forging dies
  • Gripper dies
  • Hot press dies
  • Extrusion mandrels
  • Hot header dies

Hot work punches

Main Product list



Production list
HOT WORK TOOL STEEL H13 1.2344 w302 SKD61 4Х5МФ1С
H11 1.2343 w300 SKD6 4Х5МФС
H10 1.2365 w320 / 3X3M3Ф
H21 1.2581 / SKD5 3X2B8Ф
/ 1.2367 / / /
D3 1.2080 K100 SKD1 Х12
/ 1.2601 K105 SKD11 Х12МФ
O1 1.2510 K460 SKS3 9ХВГ
O2 1.2842 K720 / /
A2 1.2363 K305 SKD12 /
A8 /   / /
D6 1.2436 K107 / /
/ / / DC53 /
S7 1.2357 / / /
L2 1.2210 / / /
  1.2767 K600 SKT6  
PLASTIC MOLD STEEL 420 1.2083 / SUS420J2  
  1.2085 /    
/ 1.2316 / /  
BEARING STEEL 52100 1.3505 / SUJ2 ШХ15


H13 H13 H13 H13



We warmly welcome clients from all over the world to cooperate with us and develop a worldwide market together. Also, we hope we can have a chance to establish a long-term business relationship with you on the basis of mutual benefits